- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- API 5CT N80 casing and tubing pipe
- API 5CT K55 casing and tubing pipe
- API 5CT J55 casing and tubing pipe
- EN10028-2 16Mo3 Boiler and Pressure Vessel steel Plate Notch impact energy
- EN10028-2 P265GH Pressure vessels steel equivalents
- EN 10210 S355J2H low alloy carbon structural steel
- EN 10210 S355J0H steel hollow materials
- GB/T 18248 34CrMo4
- GB/T 18248 35CrMo alloy steel
- 30CrMo steel Heat treatment, 30CrMo steel tube/pipe
Hot Rolled Steel C1018/20
Grade Description: A low carbon steel having a higher manganese content than mild steel and various other low carbon steels. Higher manganese makes this a better steel for carburized parts since it produces a harder and more uniform case. It also has higher mechanical properties, including Brinell Hardness, and better machining characteristics. Special manufacturing controls result in a quality product suitable for applications involving forging, heat treating, cold drawing, machining, etc.
Applications: Gears, pinions, worms, king pins, chain pins, ratchets, dogs, oil tool slips and liners, studs, anchor pins, special bolts, tie rods. Any carburized parts requiring hard surface and soft core
Analysis: C – .15/.20 Mn – .60/.90 P – .04 Max. S – .05 Max.
Mechanical Properties: (following values are average and are representative)
As Rolled | Normalized | Annealed | |
Tensile Strength (psi) | 67,000 | 66,000 | 60,000 |
Yield Point (psi) | 45,000 | 43,000 | 40,000 |
Elongation (% in 2”) | 36 | 37 | 38 |
Reduction of Area (%) | 58 | 60 | 62 |
Brinell Hardness | 137 | 137 | 121 |
Machinability: 78% of B1112. Weldability: Easily welded by all welding processes, and the resultant welds and joints are of extremely high quality. Grade of welding rod used depends on welding conditions such as thickness of section, design, service requirements, etc. Forging: Heat to 2150º – 2250º F. Normalizing: Heat to 1650º – 1750º F. Annealing: Heat to 1550º – 1650º F. Cool in furnace. Hardening: This grade will respond to any of the standard carburizing methods and subsequent heat treatments. For a hard case and a tough core, carburize at 1650º – 1700º F for approximately 8hrs, cool in box, reheat to 1400º – 1450º F, quench in water and draw at 300º – 350º F.