- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- API 5CT N80 casing and tubing pipe
- API 5CT K55 casing and tubing pipe
- API 5CT J55 casing and tubing pipe
- EN10028-2 16Mo3 Boiler and Pressure Vessel steel Plate Notch impact energy
- EN10028-2 P265GH Pressure vessels steel equivalents
- EN 10210 S355J2H low alloy carbon structural steel
- EN 10210 S355J0H steel hollow materials
- GB/T 18248 34CrMo4
- GB/T 18248 35CrMo alloy steel
- 30CrMo steel Heat treatment, 30CrMo steel tube/pipe
30CrMo steel Heat treatment, 30CrMo steel tube/pipe
30CrMo steel with high strength and toughness, high hardenability, quenching in the oil critical diameter of 15 ~ 70mm; steel thermal strength is better, below 500 ℃ with sufficient high temperature strength, but 550 ℃ when its The strength is decreased significantly; when the 30CrMo alloy elements in the lower limit of welding is quite good, but close to the upper limit of welding medium, and to be preheated to more than 175 ℃; 30CrMo steel can be machinable, cold deformation of plastic medium; In the heat treatment, there is a first type of temper brittleness in the range of 300 to 350 ° C.
30CrMo Chemical composition:
C:0.26~0.34
Si:0.17~0.37
Mn:0.40~0.70
Cr:0.80~1.10
Mo:0.15~0.25
P:≤0.035
S:≤0.035
Ni:≤0.030
Cu:≤0.030
30CrMo Heat treatment [Sample blank size (mm): 25]:
The first quenching heating temperature (℃): 880; Coolant: water, oil
Second quenching heating temperature (℃): -
Tempering heating temperature (℃): 540; Coolant: water, oil
Tensile strength (σb / MPa): ≥930
Yield point (σs / MPa): ≥785
Elongation at break (δ5 /%): ≥12
Section shrinkage (ψ /%): ≥50
Impact absorption work (Aku2 / J): ≥63
Brinell hardness (HBS100 / 3000) (annealing or high temperature tempering state) ≤ 229
30CrMo Applications:
30CrMo steel is usually used in the quenched and tempered state, when the lower limit of carbon content of steel can also be used as the requirements of the heart strength of the higher carburizing steel.
30CrMo in the steam turbine, boiler manufacturing industry for the manufacture of 450 ℃ the following fasteners,? 500 ℃ by the following high-pressure flange and nut, especially suitable for the manufacture of 300 atmospheres, 400 ℃ below the work of the catheter.