- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- API 5CT N80 casing and tubing pipe
- API 5CT K55 casing and tubing pipe
- API 5CT J55 casing and tubing pipe
- EN10028-2 16Mo3 Boiler and Pressure Vessel steel Plate Notch impact energy
- EN10028-2 P265GH Pressure vessels steel equivalents
- EN 10210 S355J2H low alloy carbon structural steel
- EN 10210 S355J0H steel hollow materials
- GB/T 18248 34CrMo4
- GB/T 18248 35CrMo alloy steel
- 30CrMo steel Heat treatment, 30CrMo steel tube/pipe
AISI 1008 carbon-low alloy steel plate Strength
1008 steel plate is AISI standard carbon-low alloy steel plate. Which contains as the main alloying elements of carbon, a small amount of Nickel, aluminum, chromium, copper, molybdenum, manganese and silicon elements for the 1008 steel plate provides excellent weldability.
AISI 1008 chemical composition:
Element |
Content (%) |
Iron, Fe |
99.31-99.7 % |
Manganese, Mn |
0.30-0.50 % |
Carbon, C |
0.10 % |
Sulfur, S |
0.050 % |
Phosphorous, P |
0.040 % |
AISI 1008 Physical properties:
Tensile strength |
340 MPa |
49300 psi |
Yield strength (depending on temper) |
285 MPa |
41300 psi |
Elastic modulus |
190-210 Gpa |
27557-30458 ksi |
Bulk modulus (typical for steel) |
200 GPa |
29000 ksi |
Shear modulus (typical for steel) |
80.0 GPa |
11600 ksi |
Poisson’s ratio |
0.27-0.30 |
0.27-0.30 |
Elongation at break (in 50 mm) |
20% |
20% |
AISI 1008 Strength:
AISI 1008 steel plate The strength of steel is often increased by the addition of small amounts of niobium or vanadium, or titanium. These elements are hardened economically by precipitation hardening. For the purpose of adding other alloying elements can also achieve the purpose of strengthening. For the hot-rolled thin steel plate, strict control of hot rolling and coiling process can achieve the required uniform strength. For cold rolled 1008 steel plates, special annealing and leveling processes are used to achieve higher strength while maintaining good formability.