You are here: Home > NewsSPA-H Smelting process

SPA-H Smelting process

Posted:2018-07-17 15:20:34

The molten iron requirement for smelting SPA-H steel must be pretreated by hot metal desulfurization. Before entering the converter, the molten iron has a sulfur content of ≤0.010% and cleans the slag on the surface of the molten iron. Nickel, copper or nickel-copper alloys are added to the converter along with the scrap. The carbon content of the converter smelting end point is ≤0.06% to prevent the steel from being peroxidized. The tapping temperature is controlled at 1 640 ~ 1 660. Before the tapping, the synthetic slag is first added to the ladle for baking. The slag plug and the slag ball double slag method are used to block the slag tapping. The tapping process is carried out by adding silicon calcium strontium, aluminum manganese titanium, silicon manganese, ferrosilicon, medium carbon ferrochrome and phosphorus iron for deoxidation alloying.

C

Si

Mn

P

S

Cu

Cr

≤0.12

0.25~0.75

≤0.60

0.070~0.150

≤0.035

0.25~0.55

0.3

Katalor Enterprises, as a SPA-H supplier in China , we can supply SPA-H stock. So if you need SPA-H price , you can contact katalor !

InquiryPlease feel free to give your inquiry in the form below. we will reply you quickly!
Name: *
E-mail: *
Country: *
Tel:
 
Company:
Language:
Product: steel plate steel pipe shipbuilding steel
Message: Please enter details such as Material, Specification, Quantity, Port, other requirments !
 
Copyright © 2018 by Shanghai Katalor Enterprises Co., Ltd. All rights reserved