305 stainless steel Processing,305 stainless steel Manufacturers

305 Stainless Steel possesses the same excellent corrosion resistance as Type 302, but has a much lower rate of work hardening. It is well suited for cold forming operations in which this low rate of work hardening is desirable. Its yield, tensile strength, and hardness increase at rates which are exceptionally low. However, its initially good elongation falls off rapidly.

305 Stainless Steel Chemical Composition
C .12 Max.
Mn 2.00 Max.
Si .040 Max.
P .030 Max.
S .750 Max.
Cr 17.00/19.00
Ni 10.50/13.00

305 stainless steel is widely used for the production of parts by free spinning and cold heading operations, and it is particularly suitable for severe cold drawing, especially where the part can be completely formed in two draws. In many instances, the intermediate anneal can be eliminated when Type 305 is used. In drawing, the metal should be allowed to slip freely through the hold-down pads, thus holding stretching to a minimum. Used widely for electronic parts and other drawn applications.

305 stainless steel Processing:
Type 305 is not hardenable by heat treatment. Anneal at 1850 - 2050°F (1010 - 1121°C), then water quench or rapid air cool.

305 stainless steel Forming:
Type 305 Stainless Steel is more readily formed, deep drawn and spun than Types 302 and 304 due to its lower work hardening rate.

Katalor Enterprises is a 305 stainless steel Manufacturers in China , for more information about 305 Stainless Steel Chemical Composition or 305 stainless steel Processing ， please contact us!