- : 0086-18317160019
- : [email protected]
- : ROOM 101 NO.16, 6TH BUILDING, 9TH LANE,GUANGYI ROAD,ZHUQIAO TOWN,PUDONG NEW AREA,SHANGHAI
- API 5CT N80 casing and tubing pipe
- API 5CT K55 casing and tubing pipe
- API 5CT J55 casing and tubing pipe
- EN10028-2 16Mo3 Boiler and Pressure Vessel steel Plate Notch impact energy
- EN10028-2 P265GH Pressure vessels steel equivalents
- EN 10210 S355J2H low alloy carbon structural steel
- EN 10210 S355J0H steel hollow materials
- GB/T 18248 34CrMo4
- GB/T 18248 35CrMo alloy steel
- 30CrMo steel Heat treatment, 30CrMo steel tube/pipe
301 stainless steel bar
301 stainless steel bars:Stainless steel bars, 301 stainless steel bars, 301 stainless round bars, 301 stainless angle steel, 301 stainless hexagonal bar, 301 stainless steel black bars,301 stainless square bar,301 stainless capstan bar , 301 stainless channel steel, 301 stainless steel bright bars.
301 is the most widely used stainless steel and heat-resistant steel. It is mainly used in food production equipment, chemical equipment through past, nuclear energy.301 (17Cr-7Ni-carbon) material, compared with 304 steel, has lower Cr, Ni content, less tensile strength and hardness increased when cold-processed, non-magnetic but after cold working.
|
1mm-500mm |
|||||||||||
|
Weight Calculation |
diameter*diameter*0.00623＝kg/m |
||||||||||
|
Mechanical Property |
Tensile Strength |
Yield Strength N/mm2 |
Elonga-tion |
Hardness |
Density |
Melting Point |
Resisti |
||||
|
≥520 |
≥205 |
≥40 |
HB |
HRB |
HV |
7.93 g·cm-3 |
1398- |
0.73 Ω·mm2·m-1 |
|||
|
≤ |
≤ |
≤ |
|||||||||
|
Chemical Composition |
Si |
C |
Mn |
Ni |
Cr |
P |
S |
||||
|
≤1.0 |
≤0.15 |
≤2.0 |
6.0-8.0 |
16.0- |
≤0.045 |
≤0.03 |
|||||
301 stainless steel Material: compared with 304 ,less Ni, Cr content makes the tensile strength and hardness increased in cold processing , non-magnetic,good weldability, but the magnetic will be there after cold working.Abrasion resistance and fatigue strength is susperior to 304 stainless steel,easy-to-shape products, and can be rapidly hardened by machining it.